Preparation and characterization of mixed hydroxy-Fe-Al pillared montmorillonite with large basal spacing

Abstract： Mixed hydroxy-Al-Fe pillared montmorillonites with large basal spacing were successfully prepared through cation-exchanging of Na+ - montmorillonite with mixed hydroxy-Al and hydroxy-Fe pillaring solutions made from hydrolysis of corresponding metal salts, followed by calcination to convert hydroxy-Al and hydroxy-Fe into intercalated polycations. According to XRD analysis, the basal spacing d(001 ) of pillared products dramatically enlarged from 12.7 A in the Na-montmorillonite to 81 A in the hydroxy-Fe -montmorillonite and 77.5 A in mixed hydroxy-Al-Fe-montmorillonite. The N2 BET surface areas of the pillared montmorillonites also greatly increased to more than 200m2/g as compared to about 27 m2/g for the Na-montmorillonite. IR analysis of hydroxy-Fe, and mixed hydroxy-Al-Fe pillared montmorillonites revealed a new absorption vibration at 1384 cm-1 wavelength. XRF elemental analysis data also showed a high content of Fe2 O3 in the hydroxy-Fe pillared montmorillonite. 作 者： ZENG Xiu-qiong    LIU Wei-ping   作者单位： ZENG Xiu-qiong(Department of Chemistry, Zhejiang University, Hangzhou 310028, China)

LIU Wei-ping(Institute of Environmental Science,Zhejiang University, Hangzhou 310028, China) 

期 刊： 环境科学学报(英文版)  ISTICSCI   Journal： JOURNAL OF ENVIRONMENTAL SCIENCES  年，卷(期)： 2004, 16(1)  分类号： X13  Keywords： hydroxy-Al    hydroxy- Fe    montmorillonite    preparation    characterization