摘要：介绍了以70％～75％ TiO2的低品位高钛渣为原料制备人造金红石的分离工艺.低品位高钛渣中MgO,FeO,CaO,Al2O3和SiO2进入杂质相,钛组分进入金红石相,金红石相中TiO2品位达到90％～95％,可满足流态化氯化对杂质的要求.1 050℃的低温预氧化与1 510℃的高温热处理促使渣中分散于各矿物相的钛组分选择性转移并富集于金红石相,金红石相析出与长大,用稀硫酸和稀盐酸实现金红石相的分离.实验结果表明,金红石矿物相平均晶粒度可以达到25 μrn,通过稀酸选择性浸出改性渣,可以获得95％TiO2品位的人造金红石.Abstract：A new technique was developed for the conversion of high titania slag,containing 70％-75％ TiO2 and with MgO,FeO,CaO,Al2O3 and SiO2 as main impurities,into a synthetic rutile,90％-95％ TiO2,which satisfies the requirements for fluidizing chlorination process with respect to impurity contents.After a pre-oxidation at around 1 042 ℃ and a heat-treatment above 1 510 ℃,the Ti components in high titania slag can be enriched into the rutile phase which can precipitate and grow,and can be separated with dilute hydrochloric and sulfuric acid,respectively.The results show that the average crystal size of rutile phase is over 25 μm,and the synthetic rutile containing more than 95％ TiO2 can be produced by selective leaching. 作者： 张力[1] 李光强[2] 张武[1] Author： ZHANG Li[1] LI Guang-qiang[2] ZHANG Wu[1] 作者单位： 东北大学材料与冶金学院,沈阳,110004武汉科技大学材料与冶金学院,武汉,430081 期 刊： 中国有色金属学报（英文版） ISTICEISCI Journal： Transactions of Nonferrous Metals Society of China 年，卷(期)： 2011, 21(10) 分类号： Q51 关键词： 高钛渣 氧化 浸出 金红石 Keywords： high titania slag oxidation leaching rutile 机标分类号： TQ1 TU5 机标关键词： 低品位 高钛渣 原料制备 金红石相 high TiO2 人造金红石 average crystal size sulfuric acid new technique 矿物相 选择性转移 选择性浸出 平均晶粒度 高温热处理 低温预氧化 Al2O3 质的要求 实验结果 分离工艺 基金项目： the Open Research Fund of Key Laboratory for Ferrous Metallurgy and Resources Utilizati 低品位高钛渣中钛组分制备金红石[期刊论文] 中国有色金属学报（英文版） --2011, 21(10)张力 李光强 张武介绍了以70％～75％ TiO2的低品位高钛渣为原料制备人造金红石的分离工艺.低品位高钛渣中MgO,FeO,CaO,Al2O3和SiO2进入杂质相,钛组分进入金红石相,金红石相中TiO2品位达到90％～95％,可满足流态化氯化对杂质的要求.1 050℃的低...【低品位高钛渣中钛组分制备金红石】相关文章：
钛钛钛04-29
含钛高炉渣综合利用与钛组分析出技术的进展05-02
钛04-29
高纯金属钛中微量氢的分析方法研究04-29
钛螺丝04-29
钛法兰04-29
高钛矿渣的粉磨特性研究04-27
从赤泥中浸出钛的研究04-26
钛材加工04-29