TiB2颗粒对喷射沉积Si-30AI复合材料显微组织的影响
摘要：结合原位反应技术和喷射沉积技术制备2％ TiB2/Si-30Al铝基复合材料.应用热力学讨论TiB2颗粒的原位反应合成原理,根据原子扩散理论分析TiB2对初晶硅的改性作用.结果表明:Si-30Al中添加2％(质量分数)的TiB2能明显细化初晶硅相.在半固态二次加热过程中,TiB2颗粒能明显抑制初晶硅的粗化、长大.Abstract：An in situ reaction and spray forming technique were employed in the synthesis of 2％ TiB2/Si-30Al composite.The formation mechanism of TiB2 particulates was explained based on thermodynamic theory.The modification of the primary Si in the Si-30Al alloy was interpreted in the light of the knowledge of atomic diffusion.The experimental results show that adding 2％ TiB2 to the Si-30Al alloy can effectively refine the primary Si.Moreover,the coarsening and growth of primary Si phase in its semi-solid state was retarded effectively due to the existence of the TiB2 particulates. 作者： 甘责生[1] 张磊[2] 贝舒瑜[2] 卢毅[2] 杨滨[2] Author： GAN Gui-sheng[1] ZHANG Lei[2] BEI Shu-yu[2] LU Yi[2] YANG Bin[2] 作者单位： 北京科技大学新金属材料国家重点实验室,北京 100083;重庆理工大学材料科学与工程学院,重庆 400050北京科技大学新金属材料国家重点实验室,北京,100083 期 刊： 中国有色金属学报（英文版） ISTICEISCI Journal： Transactions of Nonferrous Metals Society of China 年，卷(期)： 2011, 21(10) 分类号： Q946 关键词： 喷射沉积 TiB2颗粒 粗化 半固态 Keywords： spray forming TiB2 particulate coarsening semi-solid state 机标分类号： TG3 TB3 机标关键词： TiB2 颗粒 喷射沉积技术 铝基复合材料 材料显微组织 microstructure formation mechanism 初晶硅 forming technique 原位反应 in situ reaction synthesis knowledge existence 质量分数 原子扩散 理论分析 加热过程 合成原理 改性作用 基金项目： the Cultivation Fund of the Key Scientific and Technical Innovation,China，Beijing Municipal Natural Science Foundation,China TiB2颗粒对喷射沉积Si-30AI复合材料显微组织的影响[期刊论文] 中国有色金属学报（英文版） --2011, 21(10)甘责生 张磊 贝舒瑜 卢毅 杨滨结合原位反应技术和喷射沉积技术制备2％ TiB2/Si-30Al铝基复合材料.应用热力学讨论TiB2颗粒的原位反应合成原理,根据原子扩散理论分析TiB2对初晶硅的改性作用.结果表明:Si-30Al中添加2％(质量分数)的TiB2能明显细化初晶硅...【TiB2颗粒对喷射沉积Si-30AI复合材料显微组织的影响】相关文章：
喷射沉积Al-5.5Cu/TiAl3自生复合材料的微观组织及界面结构04-30
高温处理对液相气化沉积碳/碳复合材料微观组织结构及力学性能的影响04-26
多层喷射沉积的传热凝固规律研究05-02
SiC颗粒影响SiCp/Cu复合材料物理性能的研究05-02
矿渣颗粒对砂浆强度的影响04-26
苯酚对硝化颗粒污泥性能的影响04-25
超细颗粒在单个上升气泡内的沉积过程模拟04-30